PTFE-1002 wax powder

For UV, solvent-based and water-soluble paint inks and powder coatings, significantly improve surface slip and wear resistance, high temperature stability.

Product Information

Chemical composition

Teflon modified polyethylene wax

Typical physicochemical data

The data provided on this data page is only typical values and not technical indicators of the product.

Melting point:                    120/320℃

Particle size:                     D50: 4.5μm     D90: 8μm

Supply form:                        Micronized powder

Storage and transportation

Storage in cool,dry or well-ventilated place.

Application

Liquid coating and inks

Product features and advantages

The additive can reduce the friction coefficient in UV, solvent-based and water-soluble paint inks, has excellent smoothness, significantly improves the wear resistance and scratch resistance of the coating, and has good temperature resistance.

Recommended Use

Coil coating, floor coating, printing ink, high temperature matte oil, industrial coating, UV coating, plastic coating, metal baking coating.

Recommended dosage

0.3-3% additive dosage is based on the total formula, due to different formulations and process conditions, it is recommended to determine the best amount of addition before use.

Adding method and process guidance

The product can be directly dispersed in coatings and inks by high-speed stirring or grinding, and can also be added after preparation of wax paste.

Powder coatings

Features and advantages

The additive can improve the surface smoothness and scratch resistance, and improve the stain resistance of powder coatings.

Recommended dosage

0.3-2% additives based on the total formula, due to different formulations and process conditions, it is recommended to test before use to determine the best amount of addition.

Adding method and process guidance

The product is recommended to be added when the base material is premixed and then completely extruded. It can also be added to the sheet material mixed together with grinding and sifting, or added to the finished powder mixed and sifting.